Water Softening Strong Acid Cation Exchange Resin

Water Softening Strong Acid Cation Exchange Resin

Lanlang ® TC001D Is a premium grade gel type Water Softening Strong Acid Cation Exchange Resin produced by sulfonated styrene-divinylbenzene (DVB) copolymers in standard Gaussian size distribution.
Chat Now

Product Details

Water Softening Strong Acid Cation Exchange Resin

Its macroporous structure makes it can adsorb soluble organic molecules and can resist to osmotic & mechanical shock and oxidation. TC001D in sodium form could be used for water softening to reduce total hardness as well as softening of sugar solution. Combining with anion exchange resin (in hydroxide form), TC001D in hydrogen form is used for variety of demineralization application including condensate polishing.


Basic ;Features:

Application:

Water softening, demineralization

Polymer matrix structure:

Macroporous polystyrene crosslinked with divinylbenzene (DVB)

Appearance:

Tan, spherical beads

Functional Group:

Sulphonic acid

Ionic form as shipped:

Na+ ;or H+ ;when ordered as TC001D-H

;

Physical and Chemical Properties:

NO.

ITEM

SPEC


1

Total exchange capacity (eq/L)

Na+ ;form

≥1.8

H+ ;form

≥1.7



2

Moisture ;retention ;(%)

Na+ ;form

45-50

H+ ;form

48-58



3

Particle ;size ;range (%)

0.315-1.25 mm≥95


4

Whole uncracked beads after attrition ;(%)

≥96


5

Shipping weight ;(g/ml)

Na+ ;form

0.77-0.85

H+ ;form

0.74-0.80



6

Specific gravity ;(g/ml)

Na+ ;form

1.25-1.28

H+ ;form

1.16-1.24



7

Effective size (mm)

0.4 - 0.6


8

Uniformity coefficient

<1.7


9

Reversible swelling, Na+ ;→ ;H+ ;(%)

<5


;

Water Softening Strong Acid Cation Exchange Resin

Suggested Operating Conditions:

NO.

ITEM

SPEC

1

Max operating ;temperature ;

120 ;℃

2

PH range

0-14

3

Service flow rate

5-170 BV/h

4

Regenerant

10-15% NaCl, 4-10% HCl, 1-8% H2SO4


Hot Tags: Water Softening Strong Acid Cation Exchange Resin, China, suppliers, manufacturers, factory, customized, wholesale, discount, price, pricelist, quotation, free sample, made in China