TC001DU Uniform particle size macroporous type strong acid cation exchange resin
Its macroporous structure makes it can adsorb soluble organic molecules and can resist to osmotic & mechanical shock and oxidation. TC001DU in sodium form could be used for water softening to reduce total hardness as well as softening of sugar solution. Combining with anion exchange resin (in hydroxide form), TC001DU in hydrogen form is used for variety of demineralization application including condensate polishing. TC001DU is intended for reducing pressure loss and preventing system from plugging.
Basic Features:
Application: | Water softening, demineralization, low pressure loss |
Polymer matrix structure: | Macroporous polystyrene crosslinked with divinylbenzene (DVB) |
Appearance: | Tan, spherical beads |
Functional Group: | Sulphonic acid |
Ionic form as shipped: | Na+ or H+ when ordered as TC001DU-H |
Physical and Chemical Properties:
NO. | ITEM | SPEC | |
1 | Total exchange capacity (eq/L) | Na+ form | ≥1.8 |
| H+ form | ≥1.7 | ||
2 | Moisture retention(%) | Na+ form | 45-50 |
| H+ form | 48-58 | ||
3 | Particle size range (%) | 0.425-0.85 mm≥95 | |
4 | Whole uncracked beads after attrition (%) | ≥96 | |
5 | Shipping weight(g/ml) | Na+ form | 0.77-0.85 |
| H+ form | 0.74-0.80 | ||
6 | Specific gravity (g/ml) | Na+ form | 1.25-1.28 |
| H+ form | 1.16-1.24 | ||
7 | Effective size (mm) | 0.45 - 0.6 | |
8 | Uniformity coefficient | <1.25 | |
9 | Reversible swelling, Na+ → H+ (%) | <5 | |
Suggested Operating Conditions:
NO. | ITEM | SPEC |
1 | Max operating temperature | 120 ℃ |
2 | PH range | 0-14 |
3 | Service flow rate | 5-170 BV/h |
4 | Regenerant | 10-15% NaCl, 4-10% HCl, 1-8% H2SO4 |