Lanlang Non Regenerable Mixed Bed Di Resin

This is a ready-to-use resin consisting of a gel-type strong acid cation exchange resin and a strong base anion exchange resin. The product is highly converted and specially purified and blended according to specific chemical equivalents. Mixed bed is mainly used for the preparation of pure water, high purity water and fine treatment of condensed water. It requires the resin not only to have more excellent mechanical strength, but also to require the Cation and Anion resins to be completely separated during the fail-washing to prevent the "cross-contamination" of the regenerant on the resin, and to uniformly mix after regeneration. In order to achieve higher effluent quality and periodic water production.
Chat Now

Product Details

This is a ready-to-use resin consisting of a gel-type strong acid cation exchange resin and a strong base anion exchange resin. The product is highly converted and specially purified and blended according to specific chemical equivalents. Mixed bed is mainly used for the preparation of pure water, high purity water and fine treatment of condensed water. It requires the resin not only to have more excellent mechanical strength, but also to require the Cation and Anion resins to be completely separated during the fail-washing to prevent the "cross-contamination" of the regenerant on the resin, and to uniformly mix after regeneration. In order to achieve higher effluent quality and periodic water production.

mixed bed di resin


Specification

Appearance

Amber colored globular granules

Functional Groups

TC008-H : 50%

TA204-OH : 50%

Ionic form

Cation:≥99% H

Anion:≥90% OH

Volume exchange capacity (mmol/ml)

≥ 0.65

Moisture (%)

50-60

Bulk density (g/ml)

0.72-0.76

Particle size (0.315-1.25mm) (%)

≥ 95

Maximum use temperature°C

TC008-H : 100

TA204-OH : 60

PH range

1-14

mix-5


Application


Mainly used in the preparation of deionized water, ultrapure water, and other mixed bed finishing treatment of various other water treatment processes. The conductivity of the above mixed bed are all less than 0.1μs, the resistivity can reach 10 megohms, 15megohms . The cation exchange resin can be made into a dark color (close to black), so the Cation resin and Anion resin can be more easily separated when the resin is regenerated.


For sulfonated (ethylene aromatic hydrocarbon) aggregates with a molecular weight of 5,000 to 1,000,000, the treatment capacity is 10 to 800MG/1 anion exchange resin is particularly preferred. Mixed bed ion exchange resin isolated and purified egg yolk lecithin has an optimal resin ratio, in 201 and 001 ratio of 3:1, lecithin (PC) recovery rate is the highest, in the best resin ratio, get better operating conditions for temperature 10℃~20℃, sample concentration 100mg/ml. At this time, PC yield can reach more than 80%: through the penetration curve experiment, it is concluded that the maximum processing capacity of the mixed resin is 0.31g sample/ml resin, and get the PC content of the 92% (wt%) products.


Packing Style

image


Welcome to contact us! Whether you select a current product or seek engineering assistance, Lanlang is here offering satisfied services to you!

3


Hot Tags: lanlang non regenerable mixed bed di resin, China, suppliers, manufacturers, factory, customized, wholesale, discount, price, pricelist, quotation, free sample, made in China

Inquiry

You Might Also Like